TPE 65A, 良好粘结性

 

DuraGrip® DGR 6165TR

热塑性弹性体

Advanced Polymer Alloys

Technical Data

 

产品说明

 

DuraGrip® DGR6165TR is a translucent thermoplastic elastomer (TPE) formulated for excellent elastic properties and enhanced adhesion to engineered thermoplastics using insert molding, co-injection molding and co-extrusion processes. DGR6165TR bonds tenaciously to polycarbonate, polycarbonate alloys, ABS, ASA, acrylics, and cellulosic materials. It will also bond to various nylons and PET. DGR6165TR is hygroscopic and drying is recommended at 150F for 3 to 4 hours to ensure optimum aesthetics, properties and adhesion.

 

总体

 

材料状态 • 已商用：当前有效

• Processing - Injection Molding Guide (English) 

• Processing - Injection Molding Parameters (English) 

资料 1 •  Processing - Overmolding (English)

•  Technical Datasheet (English)

•  Technical Datasheet (English)

搜索 UL 黄卡 •  Advanced Polymer Alloys

供货地区 • 北美洲

性能特点 • 可粘结性 • 良好粘结性 • 延展性，高

用途 • 粘合

外观 • 半透明

加工方法 • 共挤出成型 • 注射成型

物理性能 额定值 单位制 测试方法

比重 1.04g/cm³ ASTM D471

ISO 2781

熔流率 (190°C/8.7 kg) 11g/10 min ASTM D1238

弹性体 额定值 单位制 测试方法

拉伸应力 ASTM D412

横向流量: 100%应变 3.97MPa ISO 37

流量: 100%应变 3.43MPa

横向流量: 300%应变 9.23MPa

流量: 300%应变 7.73MPa

抗张强度 ASTM D412

横向流量: 断裂 25.9MPa ISO 37

流量: 断裂 18.1MPa

伸长率 ASTM D412

横向流量: 断裂 810% ISO 37

流量: 断裂 580%

撕裂强度 3 ASTM D624

横向流量 59.5kN/m

流量 52.2kN/m

硬度 额定值 单位制 测试方法

硬度计硬度 (邵氏 A, 10 秒) 65 ASTM D2240

ISO 48

充模分析 额定值 单位制 测试方法

熔体粘度 (190°C, 294 sec^-1) 427Pa•s ASTM D3835

注射 额定值 单位制

干燥温度 65.6°C

干燥时间 3.0 到 4.0hr

加工（熔体）温度 180 到 230°C

 

 

 

 

 

 